Hastelloy合金是镍基合金。它主要是两组;一个有更多钼和另一铬的铬。两者都被称为hastelloy。它们都特别抵抗强氧化溶液,并在还原剂中具有高耐久性。由于低碳含量和焊接较低的碳化物沉淀,它们也抵抗骨间腐蚀。Hastelloy应用程序列表更长。有不同标准制造的不同形式和形状的产品,可用于各种应用。它们用于酸气井,废物处理厂,化学加工组件,纸浆和造纸工业,化工厂,热交换器,风扇和食品加工设备中的反应血管。Hastelloy性质是独特的,因为它们非常耐氧化和减少; they perform well under cryogenic temperatures and in high temperatures, resistant to wet chlorine gas, resistant to most chloride and chlorine derivatives and so on. The Hastelloy price per kg differs from product to product and you can get a full price list from us. There are many Hastelloy advantages over ordinary metal and other alloys. The resistance to localized corrosion is very high along with resistance to uniform corrosion. The resistance is also good against most salts and brackish waters. The Hastelloy abbreviation is used in the metal industry mostly instead using the full form nickel chromium molybdenum alloys. TheHastelloy合金组合物包括钼,铬,铁,钨,cobolt,锰,铜,钒,磷,硅和硫。根据合金的等级和标准,组成的不同之处。这些类和等级中的每一个都具有特定的特征和应用。Hastelloy供应商也出售所有不同的等级和不同的产品。产品范围从紧固件到管道和螺栓到轮廓环。另外,哈斯泰洛利,在超合金家庭下,许多等级是如此58必威外网 &mon。
价格 | US $ 56 / kg |
合金 | uns | 酒吧 | 管子 |
---|---|---|---|
C-4 |
N06455. |
ASTM B574 / B575 / B619 |
B622 / B619 / SB 619 / B626 / SB 626 |
C-22. |
N06022 |
ASTM B564 / B472 / B574 |
B622 / B619 / SB 619 / B626 / SB 626 |
C-2000. |
N06200. |
ASTM B564 / B472 / B574 |
B622 / B619 / SB 619 / B626 / SB 626 |
G-30. |
N06030. |
ASTM B472 / B581 |
B622 / B619 / SB 619 / B626 / SB 626 |
G-35. |
n06035. |
ASTM B564 / B472 / B574 |
B622 / B619 / SB 619 / B626 / SB 626 |
C-276. |
n10276. |
ASTM B564 / B472 / B574 |
B622 / B619 / SB 619 / B626 / SB 626 |
Hastelloy X. | N06002 | ASTM B564 / B472 / B574 | B622 / B619 / SB 619 B626 / SB 626 |
Haynes®HR-120,NAS H38X | N08120 | B407 / B514 / B515 |
CES名称 | 美国 | Werkstoff nr。 |
---|---|---|
合金名称 | uns | WNR. |
B-2 | N10665. | DIN 2.4617 |
C | n10002 | |
C-4 | N06455. | DIN 2.4610. |
C-276. | n10276. | DIN 2.4819. |
G | N06007. | |
G-3 | N06985. | DIN 2.4619. |
N | n10003. | |
S. | N06635. | |
W. | N10004. | |
X | N06002 | DIN 2.4665. |
Hastelloy®B-3®合金 | 400 - 450 DEG C(750 - 840度F) |
C-22. | 400 - 450DEG C(750 - 840度F) |
C-276. | 870 - 1230DEG C(1600 - 2250度F) |
®N合金 | 704至871deg C(1300至1600度F) |
Haynes®25合金 | 980DEG C(1800度F) |
Haynes®188合金 | 1095DEG C(2000度F) |
合金类型 | CR% | C% | CO% | W% | 莫% | V% | Ai% | TI% | NB% | Fe% | CU% | 你% | 其他 % |
---|---|---|---|---|---|---|---|---|---|---|---|---|---|
合金B. | 0.6 | 0.1 | 1.25 | - | 28. | 0.3 | - | - | - | 5.5 | - | 休息/ bal. | Mn 0.80;SI 0.70 |
合金B2 | 1 | 0.02 | 1 | - | 26.0-30.0. | - | - | - | - | 2 | - | 休息/ bal. | Mn 1.0,Si 0.10 |
合金C276 | 14.0-16.5. | 0.02 | 2.5 | 3.0-4.5 | 15.0-17.0 | 0.35 | - | - | - | 4.0-7.0 | - | 休息/ bal. | Mn 1.0;SI 0.05 |
合金X. | 22. | 0.1 | 1.5 | 0.6 | 9. | - | - | 18.5 | - | - | - | 休息/ bal. | Mn 0.6;SI 0.60 |
合金C. | 16. | 0.07 | 1.25 | 40 | 17. | 0.3 | - | - | - | 5.75 | - | 休息/ bal. | Mn 1.0;SI 0.70 |
合金C4 | 14.0-18.0 | 0.015 | 2 | - | 14.0-17.0 | - | - | 0..70 | - | 3. | - | 休息/ bal. | Mn 1.0;SI 0.08 |
合金N. | 7. | 0.06 | 0.25 | 0.2 | 16.5 | - | - | - | - | 3. | 0.1 | 休息/ bal. | MN 0.40;SI 0.25;B 0.01 |
合金S. | 15.5 | 0.02 | 2 | 1 | 14.5 | 0.6 | 0.2 | - | - | 3. | - | 休息/ bal. | Mn 0.50;SI 0.40;B0.0009;LA 0.02 |
合金F. | 22. | 0.02 | 1.25 | 0.5 | 6.5 | - | - | - | 2.1 | 21. | - | 休息/ bal. | Mn 1.50;SI 0.50 |
合金G. | 21.0-23.5. | 0.05 | 2.5 | 1 | 5.5-7.5 | - | - | - | 1.7-2.5 | 18.0-21.0. | 1.5-2.5 | 休息/ bal. | Mn 1.0-2.0;P0.04;SI 1.0; |
合金G2. | 23.0-26.0 | 0.03 | - | - | 5.0-7.0 | - | - | 0.70-1.50 | - | 休息/ bal. | 0.70-1.20 | 47.0-52.0. | Mn 1.0;SI 1.0. |
合金W. | 5. | 0.06 | 1.25 | - | 24.5 | - | - | - | - | 5.5 | - | 休息/ bal. | MN 0.050;SI 0.50 |
合金名称 | 关键点火温度 在酸化6%feCl3中 |
酸化6%FECL3临界缝隙温度 |
||
---|---|---|---|---|
°F. | °C. | °F. | °C. | |
316L. | 59. | 15. | 32. | 0. |
254SMO. | 140. | 60. | 86. | 30. |
625. | 212. | 100. | 104. | 40 |
C-276. | > 302. | > 150. | 131. | 55. |
C-22® | > 302. | > 150. | 176. | 80 |
年级 | 开裂时机 |
---|---|
316L. | 2小时 |
254SMO. | 24小时 |
625. | 1,008小时没有裂缝 |
C-276. | 1,008小时没有裂缝 |
C-22® | 1,008小时没有裂缝 |
年级 | 静止 | 流动 | ||
---|---|---|---|---|
攻击网站数量 | 最大限度。深度 | 攻击网站数量 | 最大限度。深度 | |
316L. | 答:2,B:2 | 答:1.33,B:2.27 | 答:2,B:2 | 答:0.48,B:0.15 |
254SMO. | 答:2,B:2 | 答:0.76,B:1.73 | 答:2,B:2 | 答:0.01,B:<0.01 |
625. | 答:1,B:2 | 答:0.18,B:0.04 | 答:2,B:2 | 答:<0.01,B:<0.01 |
C-276. | 答:1,B:1 | 答:0.10,B:0.13 | 答:0,B:0 | 答:0,B:0 |
C-22® | 答:0,B:0 | 答:0,B:0 | 答:0,B:0 | 答:0,B:0 |
HRB =硬度罗克韦尔“B”。
Hastelloy等级 | 床单HRB. | 盘子HRB. |
---|---|---|
C22. | 93. | 95. |
C276 | 90. | 87. |
N | 96. | - |
X | 54. | 54. |
高性能合金供应商